Demonstration Information

	Title:	Bending a Knife Blade like a Paper Clip
	Course Area:	Materials Science
	Authors:	Led Klosky

Bottom Line Up Front:

Knife blades are typically very hard and brittle. In this rapid and inexpensive demonstration, the structure of a steel knife blade is transformed through simple heating and the blade becomes capable of sustaining large deformations without rupture.

Principle: Knife blades are typically made of steels with relatively high carbon contents. These steels are also sometimes subjected to aggressive heat treatments which leave them exceptionally hard, strong and brittle. This is particularly true of utility knife blades, which are resistant to deformation (keeping them sharp longer) due to their hardness but have little toughness and thus rupture when subjected to large deformations. By heating the steel utility knife blade to an orange-hot state (perhaps 650 to 700 degrees Celsius), the steel is allowed to go through the initial stages of the annealing process, most likely leading to spheroid structure within the blade. It should be noted that this demonstration is qualitative rather than quantitative, since knowing the initial state of the blade in terms of carbon content or percent martensite, as well as what tempering and annealing went on during manufacturing, is very difficult to determine. Still, the demonstration brings out two key theoretical points. First, the heating and quenching of a sample will not lead to martensitic steels if the heat is insufficient for the formation of austenite. Second, very simple processes can lead to radical changes in material behavior, and engineers must be aware of these potential transformations when designing machines, especially for high-heat settings.

Support Formula(s):

What You Will Need:

Item Name:

Quantity:

Description:

Vice Grips

2

Standard vice grips are required (rather than pliers) to ensure that the broken halves don't fly off into the gathered crowd.

Propane Torch

1

A simple self-igniting torch will work fine.

Container of Water

1

Should be at least a pint for quenching the sample. Doesn't need to be particularly cold, since the blade has little thermal mass.

Safety Gear

1 set

Use appropriate safety gear, as the samples are sharp and hot and there is the potential for shards flying off when you break the blades.

Utility Knife Blade

2

Most simple utility blades will work; make sure to test them before class to ensure that the untreated blades break when bent, as not all blades are as brittle as you might like.

Intrepid Professor

1

This has flames, snapping steel, fiery metal plunging into cold water, etc. All the elements of real adventure.

How It's Done:

Before Class

Click to enlarge

Make sure to test this one thoroughly before trying it in class. Different knife blades can behave very differently, depending on the manufacturing process.

In Class


Click to enlarge	Click to enlarge	Click to enlarge

Begin with the as-manufactured knife blade, and dig into the student's natural knowledge about the behavior. They should be able to guess what will happen when you grab the sample with the two pairs of vice grips and bend. Let them pick which blade to test, and show them that the blade snaps neatly after just a little bit of mostly-elastic bending. MAKE SURE TO POINT THE BLADE AWAY FROM STUDENTS WHEN BENDING; THE BLADE CAN SEND SHARDS, SOMETIMES LARGE, FLYING. Then, take a fresh knife blade and heat it through with a propane torch while holding it with the vice grips. During the heating, which should take less than 1 minute, you can ask the students to give their thoughts on what is likely to happen. Having the phase diagram for steel displayed in the classroom can help fuel the discussion. The blade can then be quenched in the water without worries, and the sizzling noise is good drama for keeping student interest. The blade cools almost instantly, and can then be bent back on itself without fracture. This demonstration takes only about 4 minutes and is an excellent introduction to the topic of heat treating steels. It’s also a great way to illustrate that a mechanical designer must know about the heat treatment of steels to avoid unexpected behavior.

That Little Bit Extra:

Download additional files:

Knife Blade Movie.wmv

It is easy to relate this demonstration to what students might have seen in the Old West movies. I like to point out that a blacksmith making a horseshoe had to have a significant amount of knowledge about the heat treatment of steels (post 1870, anyway)